CEMEDINE Y600 Second Generation Acrylic adhesive - Reactive Acrylic Adhesive

2024-06-26 15:18:30 admin

CEMEDINE

Y600

Second Generation Acrylic adhesive | Reactive Acrylic Adhesive

Specifications:

Multi-purpose type

			Y600		Y600H		Y610		Y620
			Agent A	Agent B	Agent A	Agent B	Agent A	Agent B	Agent A	Agent B
Application / Properties / Features			High speed curing		High viscosity		High strength		Slow curing
Base			Acrylic resin		Acrylic resin		Acrylic resin		Acrylic resin
External appearance			Light blue	Blue	White	Gray	White	Gray	Light yellow	Blue
Viscosity		mPa･s/23°C	4,000	4,000	30,000	30,000	5,500	5,500	8,000	8,000
Mixing ratio			1:1		1:1		1:1		1:1
Pot life *1		23°C	30 s		2 min		3 min		6 min
Set time *2		23°C	3 min		4 min		6 min		20 min
Adhesive property	Tensile shear strength	MPa	23.2		19.4		26.0		21.1
Adhesive property	T-peel strength	N/mm	5.0		3.6		3.7		4.2
Curing properties	Hardness	Shore D	68		65		72		66
	Glass transfer point	°C	83		78		90		79
	Elastic modulus	MPa	767		742		935		778
	Breaking strength	MPa	16.2		14.0		19.0		16.1
	Elongation at break	%	26		8		6		25
Capacity			600g set		50g set		50g set		600g set
					10kg		600g set		2kg

High heat resistance type

			Y611BLACK S		Y612BLACK
			Agent A	Agent B	Agent A	Agent B
Application / Properties / Features			Hight strength / High heat resistance
Base			Acrylic resin		Acrylic resin
External appearance			Light yellow	Black	Light yellow	Black
Viscosity		Pa･s/23°C	3,000	3,000	15,000	15,000
Mixing ratio			1:1		1:1
Pot life *1		23°C	3 min		1 min
Set time *2		23°C	7 min		3 min
Adhesive property	Tensile shear strength	MPa	28.4		29.2
Adhesive property	T-peel strength	N/mm	4.2		4.3
Curing properties	Hardness	Shore D	84		86
	Glass transfer point	°C	123		127
	Elastic modulus	MPa	1558		1615
	Breaking strength	MPa	32.9		33.7
	Elongation at break	%	3.5		3.2
Capacity			600g set		600g set
Capacity			10kg/BIB		10kg/BIB

Flexible type

			Y618LD		Y618H		Y630D
			Agent A	Agent B	Agent A	Agent B	Agent A	Agent B
Application / Properties / Features			Flexible / Low distortion				Hight strength / High heat resistance
Base			Acrylic resin		Acrylic resin		Acrylic resin
External appearance			Red	Blue	Light yellow	Light green	Light yellow	Light green
Viscosity		Pa･s/23°C	5,000	5,000	15,000	15,000	4,000	4,000
Mixing ratio			1:1		1:1		1:1
Pot life *1		23°C	2 min		2 min 30 s		1 min 30 s
Set time *2		23°C	7 min		10 min		4 min 30 s
Adhesive property	Tensile shear strength	MPa	14.2		15.7		25.3
Adhesive property	T-peel strength	N/mm	5.9		5		4.6
Curing properties	Hardness	Shore D	47		55		83
	Glass transfer point	°C	61				118
	Elastic modulus	MPa	451				2414
	Breaking strength	MPa	10.5		10.6		32.1
	Elongation at break	%	40		51		2
Capacity			600g set		190mL set		600g set
Capacity			10kg/BIB

Conventional type SGA Y650 (*Odorous)

			Y650
			Agent A	Agent B
Base			Acrylic resin
External appearance			Blue	Red
Viscosity		mPa･s/23°C	3,220	3,320
Mixing ratio			1:1
Pot life *1		23°C	2 min 30 s
Set time *2		23°C	4 min 30 s
Adhesive property	Tensile shear strength	MPa	23.8
Adhesive property	T-peel strength	N/mm	4.6
Curing properties	Hardness	Shore D	60
	Glass transfer point	°C	83
	Elastic modulus	MPa	740
	Breaking strength	MPa	16.1
	Elongation at break	%	25
Capacity			2.5kg