CEMEDINE CEMEDINE 3000 Series Instant Adhesives
2024-06-26 15:25:23
admin
CEMEDINE
CEMEDINE 3000 Series
Instant Adhesives
Specifications:
(3000RX series)
| 3000RX | 3000RXF | 3000RXL | 3000RXM | 3000RXH | |||
|---|---|---|---|---|---|---|---|
| Application / Properties / Features | Super-quick curing adhesion resistant material | ||||||
| Base | Ethyl-2-cyanoacrylate | Ethyl-2-cyanoacrylate | Ethyl-2-cyanoacrylate | Ethyl-2-cyanoacrylate | Ethyl-2-cyanoacrylate | ||
| External appearance | Colorless transparent | Colorless transparent | Colorless transparent | Colorless transparent | Colorless transparent | ||
| Non volatiles | % | 100 | 100 | 100 | 100 | 100 | |
| Flash point | °C | 75 | 75 | 75 | 75 | 75 | |
| Viscosity | mPa･s/23°C | 3 | 15 | 100 | 300 | 1000 | |
| Specific gravity | g/cm3 | 1.21~1.25 | 1.21~1.25 | 1.21~1.25 | 1.21~1.25 | 1.21~1.25 | |
| Set time | 23°C | 5 sec | 5 sec | 5 sec | 5 sec | 15 sec | |
| Glass transfer point | °C | 175~182 | 175~182 | 175~182 | 175~182 | 175~182 | |
| linear expansion coefficient | ppm/K | 1.26 | 1.26 | 1.26 | 1.26 | 1.26 | |
| Volume resistivity | Ω･cm/30°C | 8.6x1012 | 8.6x1012 | 8.6x1012 | 8.6x1012 | 8.6x1012 | |
| Insulation breakdown voltage | kv/0.1mm | 14.6 | 14.6 | 14.6 | 14.6 | 14.6 | |
| Dielectric constant | 10Mc, 10℃ | 3.54 | 3.54 | 3.54 | 3.54 | 3.54 | |
| Dielectric loss tangent | 10Mc, 10℃ | 0.068 | 0.068 | 0.068 | 0.068 | 0.068 | |
| Tensile shear strength | MPa | 13 | 13 | 13 | 13 | 13 | |
| Method of applying | Apply right from the container | Apply right from the container | Apply right from the container | Apply right from the container | Apply right from the container | ||
| Capacity | 20g | 20g | 20g | 20g | 50g | ||
| 50g | 50g | 50g | |||||
Shock resistance type : 3000DX series
Peel strength (3000DX series)
(N/mm)
| Adherends | 3000DXL | 3000DXH |
|---|---|---|
| Steel plate (grinding) | 1.96 | 3.12 |
| Steel plate | 1.16 | 2.76 |
| Aluminum | 3.12 | 3.12 |
| Stainless steel | 1.16 | 3.52 |
| Copper | 0.80 | 1.56 |
| Zinc | 1.56 | 1.96 |
Test conditions
1) T-formed peeling strength is 50mm/min. in conformity to JIS K6854. 50mm/min
2) After being degreased with acetone and toluene at a mixing ratio of 1 to 1, each test piece is cured at the normal temperature for 48 hours; then it is measured.
Property (3000DX series)
| 3000DXF | 3000DXLL | 3000DXL | 3000DXH | |||
|---|---|---|---|---|---|---|
| Application / Properties / Features | High-strength, impact-resistant | |||||
| Base | Ethyl-2-cyanoacrylate | Ethyl-2-cyanoacrylate | Ethyl-2-cyanoacrylate | Ethyl-2-cyanoacrylate | ||
| External appearance | Colorless transparent | Colorless transparent ~ Translucent jelly | Colorless transparent ~ Translucent jelly | Colorless transparent ~ Translucent jelly | ||
| Non volatiles | % | 100 | 100 | 100 | 100 | |
| Flash point | °C | 75 | 75 | 75 | 75 | |
| Viscosity | mPa･s/23°C | 10 | 100 | 300 | 3000 | |
| Specific gravity | g/cm3 | 1.05 | 1.05 | 1.05 | 1.05 | |
| Set time | 23°C | 30 sec | 45 sec | 60 sec | 75 sec | |
| Tensile shear strength | MPa | 21 | 21 | 21 | 22 | |
| T-peel strength | N/mm | 2.0 | 2.5 | 3 | ||
| Method of applying | Apply right from the container | Apply right from the container | Apply right from the container | Apply right from the container | ||
| Capacity | 20g | 20g | 20g | 50g | ||
| 50g | ||||||